Large-caliber thin-wall Ti35 titanium alloy seamless pipe and preparation method thereof
A technology for seamless pipes and titanium alloys is applied in the field of large-diameter thin-walled Ti35 titanium alloy seamless pipes and their preparation, which can solve the problems of immature technology, no production method, and high production costs, reducing processing times, The effect of improving material utilization rate and high material utilization rate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0028] Example 1
[0029] The large diameter thin wall Ti35 titanium alloy seamless pipe of the present embodiment consists of the following mass content: Ta 5.6%, Fe0.01%, C 0.018%, N 0.003%, H 0.0011%, O 0.10%, and the margin is Titanium and inevitable impurities;
[0030] The method of preparing the large diameter thin wall Ti35 titanium alloy seamless pipe of the present embodiment includes the steps of:
[0031] Step 1, the billet was prepared: 5 rods of Ti35 titanium alloy ingots having a diameter of 640 mm were performed to obtain a bar blank having a diameter of 570 mm;
[0032] Step 2, the billet was prepared: The billet obtained in the step first was placed in the heating furnace at 600 ° C for 1 h, then continued to heat up to 800 ° C for 2 h, then warmed to 960 ° C for 3 hours, afterward, the diameter was performed. 580mm, wall thickness is 50 mm, a mass of greater than 6000 mm;
[0033] Step three, the tube billet treatment: Take a homogenized treatment in step I 2 homog
Example Embodiment
[0037] Example 2
[0038] The large diameter thin wall Ti35 titanium alloy seamless pipe of this embodiment consists of the following mass content: Ta 6.48%, Fe 0.023%, C 0.012%, N 0.090%, and the remaining amount is titanium. And inevitable impurities;
[0039] The method of preparing the large diameter thin wall Ti35 titanium alloy seamless pipe of the present embodiment includes the steps of:
[0040] Step 1, the billet preparation: 7-flaud forged Ti35 titanium alloy ingot with a diameter of 640 mm is performed to obtain a bar blank having a diameter of 200 mm;
[0041] Step 2, the billet was prepared: The billet obtained in the step one was placed in the heating furnace at 600 ° C for 1 h, then continued to warm up to 800 ° C for 1 h, then warmed to 860 ° C for 2 h, then the diameter was perforated. It is 210mm, a wall thickness of 22 mm, a length of greater than 6000 mm;
[0042] Step 3, the tube blank: The segment obtained in step II is homogenized at 850 ° C insulation for 2 ho
Example Embodiment
[0046] Example 3
[0047] The large diameter thin wall Ti35 titanium alloy seamless pipes of the present embodiment consists of the following mass content: Ta 6.2%, Fe0.013%, C 0.012%, N 0.089%, and the remaining amount is Titanium and inevitable impurities;
[0048] The method of preparing the large diameter thin wall Ti35 titanium alloy seamless pipe of the present embodiment includes the steps of:
[0049] Step 1, the billet is prepared: 6-flake forging in a Ti35 titanium alloy ingot having a diameter of 640 mm is performed to obtain a bar blank having a diameter of 400 mm;
[0050] Step 2, the billet was prepared: The billet obtained in the step one was placed in the heating furnace at 600 ° C for 1 h, then continued to warm up to 800 ° C for 1 h, then warmed to 860 ° C for 2 h, then the diameter was perforated. Take 410mm, wall thickness of 55 mm, a mass of greater than 4000 mm;
[0051] Step three, tube blank: Take a homogenized treatment in step I 2 homogenize at 900 ° C, afte
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap