3c1b coating, method of applying the same and substrate coated therewith
a multi-layer coating and substrate technology, applied in the direction of coatings, anti-corrosion paints, polyester coatings, etc., can solve the problems of affecting the leveling arrangement of aluminum powders, failure to achieve strong sparkling effect, and the coating will not perform the function of an electro-plated
Inactive Publication Date: 2019-05-23
PPG COATINGS TIANJIN
View PDF0 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
The present invention is about a multi-layer coating system that includes three different coatings on a substrate. The first coating is made of a polyester resin and an amino resin, the second coating is made of a nitro-modified acrylic resin and electro-plated aluminum powders, and the third coating is made of an acrylic resin and an anti-sagging resin. The process of applying these coatings involves applying them in a specific order, baking them to dryness, and resulting in a high-quality multi-layer coating system that has good adhesion and appearance. The technical effects of this invention include improved protection and durability of the substrate, as well as better appearance and functionality of the coating system.
Problems solved by technology
For the 3C1B system comprising an electro-plated silvery color coat, as the electro-plated silvery color coat has a quite thin thickness, the base coat and top coat (clear coat) are prone to eroding and blending into the color coat, which would considerably affect the leveling of arrangement of aluminum powders.
As a result, the coat upon application will lose the mirror effect and lead to failure of strong sparkling effect.
Such a coat will not perform the function of an electro-plated silvery coat.
Furthermore, the resin participating in orientation of aluminum powders is present in a lower amount and fails to reorient the aluminum powders during leveling.
Therefore, this will impart more requirements on the basecoat matching with the electro-plated silvery color coat, thereby significantly increasing difficulty in developing coatings used as a basecoat.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
examples
[0061]The following examples are presented to demonstrate the general principles of the invention. The invention should not be considered as limited to the specific examples presented. All parts and percentages in the examples are by weight unless otherwise indicated.
[0062]The first coating composition as the base coat was prepared from the components and amounts listed in Table 1.
TABLE 1Formulation of the first coating compositionExample 1Example 2Example 3Components(wt %*)(wt %)(wt %)Polyester resin38.543.533.5Amino resin152010Leveling agent111solvent301540Adhesion promoter0.50.50.5Colorant paste151515*based on the total weight of the first coating composition (g):Polyester resin: GALSTAFF 205, Tg 85-125° C., supplied by GALSTAFF;Amino resin: CYMEL-615, supplied by Zhanxin;Leveling agent, BYK-358N, supplied by BYK;Adhesion promoter: ADHERANT 1121, supplied by DEUCHEM;Solvent: xylene, trimethylbenzene, and tetramethylbenzene;Colorant paste: JET BLACK TINTER, supplied by PPG.
[0063]T...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| particle size | aaaaa | aaaaa |
| particle size | aaaaa | aaaaa |
Login to view more
Abstract
Provided is a multi-layer coating system, comprising a first coating composition, a second coating composition, and a third coating composition, wherein the first coating composition comprises a polyester resin and an amino resin, the second coating composition comprises a nitro-modified acrylic resin and electro-plated aluminum powders, and the third coating composition comprises an acrylic resin and an anti-sagging resin. Also provided are a method of coating a substrate with the multi-layer coating system and the substrate coated therewith.
Description
FIELD OF INVENTION[0001]The present invention relates to a 3C1B multi-layer coating system, a method of applying the 3C1B coating system and a substrate coated therewith, and in particular to a 3C1B multi-layer coating system comprising an electro-plated silvery coat, a method of applying the 3C1B coating system and a substrate coated therewith.BACKGROUND OF THE INVENTION[0002]A three-coat one-bake (3C1B) process to apply a multi-layer coating to the body or parts of an automotive is usually used in the industrial paint application to save energy and increase production efficiency. The process comprises applying a first layer of a coating and flash-drying the first layer of the coating at an ambient temperature; then applying a second layer of a coating and flash-drying the second layer of the coating at an ambient temperature; and applying a third layer of a coating, wherein the three layers of coatings are applied in a wet-on-wet-on-wet manner. Such process can shorten the product...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more Patent Type & Authority Applications(United States)
IPC IPC(8): C09D5/38B05D7/00C09D5/10B05D7/14C08K9/02
CPCC09D5/38B05D7/572C09D5/103B05D7/14C08K9/02B05D2601/08C08K2003/0812B05D3/0254B05D5/061B05D7/16B05D7/24B05D7/582B05D7/584B05D2202/25B05D2320/00B05D2451/00B05D2501/00B05D2502/005B05D2508/00B05D2601/10B05D2602/00C08K3/08C08L2205/025C08L2205/03C09D133/00C09D167/00C09D7/61B05D2420/01B05D2420/02B05D2420/03C08L61/20C08L33/00C09D133/066C09D133/14C09D7/62C09D7/69
Inventor NIU, XINBOCAO, JIANZHANG, GEHONGTONG, HONGLIU, YAN
Owner PPG COATINGS TIANJIN
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap