Thermal-insulation coating
A technology of thermal insulation coating and silicon material, applied in the field of thermal insulation coating, can solve the problems of easy falling off, flammability and corrosion of foam board, and achieve the effect of easy promotion, convenient construction and strong adhesion
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Examples
Embodiment 1
[0014] (1) Take the following raw materials by weight: 2.5 parts by weight of magnesium oxide, 31 parts by weight of silicon-containing materials, 32 parts by weight of vermiculite powder, 5 parts by weight of perlite powder, 6 parts by weight of mica powder, 3 parts by weight of binder, vegetable protein 0.5 parts by weight of glue;
[0015] (2) Add the above-mentioned raw materials by weight into water, the addition amount is 20% of the weight of the raw materials (excluding water), and mix under the condition of 45-50°C;
[0016] (3) Introduce a foaming agent while mixing, and prepare a coating slurry after uniform microbubbles are formed in the material;
[0017] (4) Mix the coating slurry evenly and apply it on the outer layer of the material to form a thermal insulation coating.
[0018] Preferably, the silicon-containing material in the embodiment is one of silicon dioxide, silicate, calcium silicate, and magnesium silicate.
[0019] Preferably, the binder in the embodim
Embodiment 2
[0021] (1) Take the following raw materials by weight: 3.5 parts by weight of magnesium oxide, 30 parts by weight of silicon-containing materials, 30 parts by weight of vermiculite powder, 5 parts by weight of perlite powder, 7 parts by weight of mica powder, 4 parts by weight of binder, vegetable protein 0.5 parts by weight of glue;
[0022] (2) Add the above-mentioned raw materials by weight into water, the addition amount is 20% of the weight of the raw materials (excluding water), and mix under the condition of 45-50°C;
[0023] (3) Introduce a foaming agent while mixing, and prepare a coating slurry after uniform microbubbles are formed in the material;
[0024] (4) Mix the coating slurry evenly and apply it on the outer layer of the material to form a thermal insulation coating.
[0025] Preferably, the silicon-containing material in the embodiment is one of silicon dioxide, silicate, calcium silicate, and magnesium silicate.
[0026] As preferably, the binding agent in t
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap