Cast steel and method for preparing same
A technology of cast steel and molten steel, applied in the field of cast steel and the preparation of the cast steel, can solve the problems of easy deformation, low strength and elongation of cast steel, unable to meet market requirements, etc., and achieve high elongation and high strength elongation. rate effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
Specific Example 1
[0010] This specific embodiment is a cast steel containing the following chemical components by weight percentage: C: 0.21%, Si: 0.42%, Mn: 1.06%, Ni: 0.49%, Cr: 0.16%, Mo: 0.04%, P= 0.023%, S=0.020%, the balance is iron, and the carbon equivalent is 0.458%.
[0011] The preparation method of the low-alloy cast steel in this specific embodiment includes the following steps: 1. According to the chemical composition range given, use scrap steel and pig iron as ingredients; 2. Load the prepared materials into an electric arc furnace for smelting and smelting During the process, ferrosilicon, ferromanganese, electrolytic nickel, and ferrochrome are added to adjust the chemical composition; 3. The molten steel obtained by smelting is poured into castings; 4. Normalizing treatment. To measure, its mechanical properties are: σ b =576Mpa,σ s =371Mpa, δ=19.8%, Brinell hardness HB=171.
Example Embodiment
Specific Example 2
[0012] This specific embodiment is a cast steel containing the following chemical components by weight percentage: C: 0.19%, Si: 0.40%, Mn: 1.10%, Ni: 0.48%, Cr: 0.12%, Mo: 0.04%, P= 0.026%, S = 0.022%, the balance is iron, and the carbon equivalent is 0.436%.
[0013] The preparation method of the low-alloy cast steel in this specific embodiment includes the following steps: 1. According to the chemical composition range given, use scrap steel and pig iron as ingredients; 2. Load the prepared materials into an electric arc furnace for smelting and smelting During the process, ferrosilicon, ferromanganese, electrolytic nickel, and ferrochrome are added to adjust the chemical composition; 3. The molten steel obtained by smelting is poured into castings; 4. Normalizing treatment. To measure, its mechanical properties are: σ b =573Mpa,σ s =375Mpa, δ=20.4%, Brinell hardness HB=166.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap