Selective hydrogenation catalyst
一种选择加氢、催化剂的技术,应用在通过选择性加氢精制、物理/化学过程催化剂、金属/金属氧化物/金属氢氧化物催化剂等方向,能够解决单烯选择性不高等问题,达到制备周期短、好应用前景、活性高的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment l
[0030] Prepare a nickel acetate solution with a concentration of 0.1mol / L, add a certain amount of LaNO with a concentration of 0.1mol / L 3 , so that the molar ratio of La to Ni is 1:30, the mixed solution is stirred and mixed evenly with a certain amount of aluminum sulfate / titanium sulfate mixed sol with a solid content of 20%, and the atomic ratio of Ti:Al in the sol is 0.12. Then prepare KBH with a concentration of 1.5mol / L 4 solution (B:Ni=3.0:1.0, atomic ratio), at 15°C, under the protection of Ar gas, the KBH 4 Drop it into the mixed solution of mixed sol and nickel salt at a speed of 1-6ml / min until no gas is generated in the reaction. Nickel constituted 15% by weight of the catalyst. The resulting catalyst is denoted as Al.
Embodiment 2
[0032] Prepare a nickel chloride solution with a concentration of 0.1mol / L, and add a certain amount of CeCl with a concentration of 0.1mol / L 2 , the molar ratio of Ce to Ni is 1:9, the mixed solution is stirred and mixed evenly with a certain amount of aluminum sulfate / titanium sulfate mixed sol with a solid content of 20%, and the atomic ratio of Ti:Al in the sol is 0.23, Then prepare KBH with a concentration of 1.5mol / L 4 solution (B:Ni=3.0:1.0, atomic ratio), at 20°C, under the protection of Ar gas, the KBH 4 Drop it into the mixed solution of mixed sol and nickel salt at a speed of 1-6ml / min until no gas is generated in the reaction. Nickel constituted 15% by weight of the catalyst. The resulting catalyst is designated A2.
Embodiment 3
[0034] Prepare a nickel nitrate solution with a concentration of 0.1mol / L, and add a certain amount of CrCl with a concentration of 0.1mol / L 3 , the molar ratio of Cr and Ni is 3:97, the mixed solution is stirred and mixed evenly with a certain amount of aluminum nitrate / titanium nitrate mixed sol with a solid content of 20%, and the atomic ratio of Ti:Al in the sol is 0.34, .Reconstitute KBH with a concentration of 1.5mol / L 4 solution (B:Ni=3.0:1.0, atomic ratio), at 25°C, under the protection of Ar gas, the KBH 4 Drop it into the mixed solution of mixed sol and nickel salt at a speed of 1-6ml / min until no gas is generated in the reaction. Nickel constituted 15% by weight of the catalyst. The resulting catalyst is designated A3.
PUM
Property | Measurement | Unit |
---|---|---|
solid containing ratio | aaaaa | aaaaa |
composition ratio | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap