Stretch-proof and easily-degradable plastic bag and preparation method thereof
An easy-degradable and stretch-resistant technology, which is applied in stretch-resistant and easily degradable plastic bags and its preparation field, can solve the problems of easy breakage and low stretching of degradable plastic bags, and achieve improved water resistance and improved The effect of less stretching and higher success rate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0052] Example 1
[0053] A stretch-resistant and easily degradable plastic bag, the preparation method of which comprises the following steps:
[0054] S1: pulverize the kraft paper to 60-80 mesh to obtain kraft paper powder;
[0055] S2: Ball milling of polyvinyl alcohol, starch, photodegradation agent, kraft paper powder and citric acid ester, the ball milling speed is 240rad / min, and the ball milling time is 1.5h to obtain the spare material; Pentadiene iron, citrate is tributyl citrate;
[0056] S3: send the spare material into the film blowing machine, the temperature of the material barrel of the film blowing machine is controlled at 165 °C, the temperature of the die mouth is controlled at 180 °C, and the inflation ratio is 2 to obtain a plastic film;
[0057] S4: Slitting and sealing the plastic film to obtain a stretch-resistant and easily degradable plastic bag;
[0058] Wherein, the specific addition amount of each raw material in this example refers to Example 1
Example Embodiment
[0059] Example 2
[0060] A stretch-resistant and easily degradable plastic bag, the preparation method of which comprises the following steps:
[0061] S1: pulverize the kraft paper to 60-80 mesh to obtain kraft paper powder;
[0062] S2: Ball milling of polyvinyl alcohol, starch, photodegradation agent, kraft paper powder and citric acid ester, the ball milling speed is 260rad / min, and the ball milling time is 1.2h, to obtain the spare material; in this embodiment, the photodegradation agent adopts a bicyclic Pentadiene iron, citrate is tributyl citrate;
[0063] S3: send the spare material into the film blowing machine, the temperature of the barrel of the film blowing machine is controlled at 160 °C, the temperature of the die mouth is controlled at 175 °C, and the inflation ratio is 2.5 to obtain a plastic film;
[0064] S4: Slitting and sealing the plastic film to obtain a stretch-resistant and easily degradable plastic bag;
[0065] Wherein, the specific addition amou
Example Embodiment
[0066] Example 3
[0067] A stretch-resistant and easily degradable plastic bag, the preparation method of which comprises the following steps:
[0068] S1: pulverize the kraft paper to 60-80 mesh to obtain kraft paper powder;
[0069] S2: Ball milling of polyvinyl alcohol, starch, photodegradation agent, kraft paper powder and citric acid ester, the ball milling speed is 280rad / min, and the ball milling time is 1h, to obtain the standby material; in this embodiment, the photodegradation agent adopts dicyclopentane Diene iron, citrate is tributyl citrate;
[0070] S3: send the spare material into the film blowing machine, the temperature of the material barrel of the film blowing machine is controlled at 155°C, the temperature of the die mouth is controlled at 170°C, and the inflation ratio is 3 to obtain a plastic film;
[0071] S4: Slitting and sealing the plastic film to obtain a stretch-resistant and easily degradable plastic bag;
[0072] Wherein, the specific addition
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap