High-temperature bearing steel and cleaning and homogenizing preparation method thereof
A high-temperature bearing and homogenization technology, applied in the field of alloy steel, to achieve the effects of high hardness, excellent fatigue performance, and high rotational bending fatigue ultimate strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0028] According to the scope of the chemical component design designed in the present invention, 4 furnaces (numbers 1 to 4) inventive steel is smented on a 1 ton vacuum induction furnace and a vacuum buffer, and 3 groups of Cr-Mo-V contrast steel (number 5 ~ 7) ), The specific chemical composition is shown in Table 1, the invention is significantly lower than the contrast steel. Invention Steel double vacuum smelting, poured into a ingot, and blessed with high temperature diffusion, upset deformation and forging, and final forged rolling into φ120 and φ80 rods. Steel and comparison steel processed into standard room temperature tensile samples, Xia ratio gap impact sample, hardness sample, gold phase sample, rolling contact fatigue sample, and screwing fatigue samples. The steel and contrast steel of the present invention take the heat treatment system: After the quenching of 1090 ° C is deeply cold by tempering, the samples of the grain size are measured by grinding, polishing, an
PUM
Property | Measurement | Unit |
---|---|---|
Tensile strength | aaaaa | aaaaa |
Surface hardness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap