On-line quenching and tempering technology of seamless steel tube
一种无缝钢管、调质的技术,应用在制造工具、炉、热处理设备等方向,能够解决影响调质的最终结果、自然冷却速度慢、降低产品质量等问题,达到提高钻孔深度和钻进速度、壁厚不均偏差小、提高纯净度的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] In this embodiment, a seamless steel pipe includes the following components in weight percentage, C: 0.38-0.43%, Si: 0.17-0.35%, Mn: 0.70-0.90%, P≤0.015%, S≤0.010%, Cr : 0.90~1.10%, Mo: 0.15~0.25%, Cu: ≤0.10%, Ni: ≤0.10%, AS≤0.015%, Sn≤0.015%, Sb≤0.010%, Pb≤0.008%, Bi≤0.010%, The balance is Fe.
[0022] This seamless steel pipe is quenched and tempered, and its steps are as follows:
[0023] (1) Quenching, the temperature is rapidly raised to 910°C at a speed of 30°C / s, and then rapidly cooled to about 310°C by spraying at a cooling rate of 210°C / s, and then sprayed twice to below 80°C;
[0024] (2) Tempering, the heating rate is 20-30°C / s, the temperature is raised to 630°C, and air-cooled after heat preservation;
[0025] The heating process adopts electric induction heating.
[0026] In this embodiment, a quenching liquid is used for cooling in step (1).
[0027] In this embodiment, the quenching liquid is a polyether polymer quenching liquid, wherein the mass c...
Embodiment 2
[0029] In this embodiment, a seamless steel pipe includes the following components in weight percentage, C: 0.38-0.43%, Si: 0.17-0.35%, Mn: 0.70-0.90%, P≤0.015%, S≤0.010%, Cr : 0.90~1.10%, Mo: 0.15~0.25%, Cu: ≤0.10%, Ni: ≤0.10%, AS≤0.015%, Sn≤0.015%, Sb≤0.010%, Pb≤0.008%, Bi≤0.010%, The balance is Fe.
[0030] This seamless steel pipe is quenched and tempered, and its steps are as follows:
[0031] (1) Quenching, the temperature is rapidly raised to 910°C at a rate of 30°C / s, and then rapidly cooled to below 80°C by spraying once at a cooling rate of 210°C / s;
[0032] (2) Tempering, the heating rate is 20-30°C / s, the temperature is raised to 630°C, and air-cooled after heat preservation;
[0033] The heating process adopts electric induction heating.
[0034] In this embodiment, a quenching liquid is used for cooling in step (1).
[0035] In this embodiment, the quenching liquid is a polyether polymer quenching liquid, wherein the mass content of the polyether polymer mat...
PUM
Property | Measurement | Unit |
---|---|---|
ellipticity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap