The invention relates to anti-corrosion acrylic acid epoxy resin powder paint for ceramic. The paint comprises the following raw materials: glycidyl methacrylate, polyol, azobisisobutyronitrile, monoacid, di-tert-butyl peroxide, dicyclopentadiene, an initiator, maleic anhydride, epoxy resin, zinc oxide, a flatting agent, 1-o-tolylbiguanide, dodecanedioic acid, 2-mercaptobenzothiazole and titanium dioxide. According to the paint, the melting point is 200-220 DEG C, the density is 135-145g/cm<3>, and the paint has no abnormity after being soaked in 5% hydrochloric acid solution for 20-30d; the glossiness is 140%-150%, and after the artificial accelerated aging is implemented for 500h, the gloss retention rate is 94-98%; the shore hardness is 50-70H, the drying time is 20-30min, the paint cannot bubble or crinkle after being soaked in saturated calcium hydroxide for 15-35d, and the scrubbing resistance times are 1800-2200.