Method of preparing chromatographic materials
一种吸附剂、单乙烯的技术,应用在制备新的树脂用于高选择性色谱层析领域,能够解决材料损失大、产品成本高、产物收率低等问题
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment
[0075] The 250 ml flask was equipped with a stirrer, an argon inlet tube and a dropping funnel. The flask was poured with 120 mL of 20% sodium sulfate and bubbled with argon for 20 minutes. At the same time, 2 ml of methyl phenylacrylate, 3 ml of methacrylic acid, 0.921 g of HTA, 2 ml of alcohol laurate, 11 ml of butanol, 11 ml of cyclohexanol were added. After the comonomer is dissolved, 0.06 g of 1,1'-azocyclohexane is added. The polymerization reaction was carried out at a temperature of 60° C. for 10 minutes to obtain a viscous prepolymer. The prepolymer was dispersed into 120 ml of 20% sodium sulfate. The temperature was maintained at 60°C to 70°C for 30 minutes. The temperature was then raised to 100°C and the reaction was continued at this temperature for 1 hour. In the next step, the resulting spherical particles are separated from the dispersion after cooling to a temperature below about 25°C. The particles were then washed with glacial acetic acid, then water, t...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap