Solvent-free type colorized anti-skid road surface adhesive
A solvent-free, adhesive technology, applied in the direction of adhesive additives, adhesive types, polyurea/polyurethane adhesives, etc., can solve the problems of long curing time, loose bonding of components, and short pot life, etc. Achieve the effect of reducing the time for external release, accelerating the curing speed and extending the pot life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] The solvent-free colored non-slip road adhesive includes the following components by weight:
[0017] 73 parts of polyether amine crosslinking compound, 25 parts of polyisocyanate, and 2 parts of catalyst. Wherein, the polyisocyanate is diphenylmethane diisocyanate, and the catalyst comprises the following components by weight:
[0018] 1 part zinc 2-ethylhexanoate and 1 part 2-ethylhexanoic acid.
[0019] The polyether amine crosslinking compound includes the following components by weight:
[0020] 45 parts of polyoxypropylene glycol, 9 parts of amine crosslinking agent, 35 parts of polyether, 5 parts of mica powder, 1 part of iron oxide red paste and 3 parts of auxiliary agent.
[0021] Auxiliaries include the following components in weight ratio:
[0022] 1.5 parts of polyether modified silicone copolymer and 1.5 parts of acrylate polymer.
[0023] Since the solid content of the polyether amine crosslinking compound and polyisocyanate in the solvent-free colored no
Embodiment 2
[0025] The components of the solvent-free colored non-slip road surface adhesive of this embodiment are basically the same as those of Example 1, the difference between the two is that the weight ratio of each component is different. In this embodiment, there are 68.5 parts of polyether amine crosslinking compound, 30 parts of polyisocyanate, and 1.5 parts of catalyst. Wherein, the polyisocyanate is diphenylmethane diisocyanate, and the catalyst comprises the following components by weight:
[0026] 1 part of zinc 2-ethylhexanoate and 0.5 part of 2-ethylhexanoic acid.
[0027] The polyether amine crosslinking compound includes the following components by weight:
[0028] 42 parts of polyoxypropylene glycol, 8 parts of amine crosslinking agent, 37 parts of polyether, 6 parts of mica powder, 0.5 part of iron oxide red paste and 2 parts of auxiliary agent.
[0029] Auxiliaries include the following components in weight ratio:
[0030] 1 part of polyether modified siloxane copolym
Embodiment 3
[0032] The components of the solvent-free colored non-slip road surface adhesive of this embodiment are basically the same as those of Example 1, the difference between the two is that the weight ratio of each component is different. In this embodiment, there are 74 parts of polyether amine crosslinking compound, 25 parts of polyisocyanate, and 1 part of catalyst. Wherein, the polyisocyanate is diphenylmethane diisocyanate, and the catalyst comprises the following components by weight:
[0033] 0.5 parts of zinc 2-ethylhexanoate and 0.5 parts of 2-ethylhexanoic acid.
[0034] The polyether amine crosslinking compound includes the following components by weight:
[0035] 47 parts of polyoxypropylene glycol, 10 parts of amine crosslinking agent, 32 parts of polyether, 4 parts of mica powder, 0.7 parts of iron oxide red paste and 2.5 parts of additives.
[0036] Auxiliaries include the following components in weight ratio:
[0037] 1.5 parts of polyether modified siloxane copolym
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap