Antistatic anti-flaming PC/ABS compound material and preparation method thereof
A composite material, antistatic technology, applied in the field of antistatic flame retardant PC/ABS composite material, can solve the problems of limited practical application, decreased thermal stability of PC, high price of antistatic agent, etc., to achieve excellent antistatic properties, reduce Influence, little effect on mechanical properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1~5 and comparative example 1~4
[0040] According to Table 1, formula PC resin, ABS resin, flame retardant, toughening agent, antistatic agent, antioxidant and other additives are put into the mixer and blended until uniform, and the obtained premix is put into the twin screw extruder Melt mixing and extrusion granulation are performed to obtain the antistatic and flame-retardant PC / ABS composite material of the present invention. Among them, the screw length-diameter ratio of the twin-screw extruder is 40:1, the barrel temperature is 260-280°C, and the screw speed is 400-500rpm.
[0041] The antistatic property, flame retardancy and notched cantilever beam impact strength of the prepared PC / ABS composite material were tested. The reference standards or methods for the test are as follows:
[0042] (1) Antistatic property: The surface resistivity is used to characterize the antistatic properties of the material. A 2mm thick molded square plate is adjusted for 24 hours at 23°C and 50% humidity, and the surface re...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap