High-hardness polyethylene floor and preparation method thereof
A polyethylene and high-hardness technology, which is applied in the field of high-hardness polyethylene flooring and its preparation, can solve the problems of unproduced foamed floors, and achieve the effect of high bending strength and high hardness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0014] Example 1
[0015] The high-hardness polyethylene floor is composed of the following materials by weight: 25 parts of polyvinyl chloride resin SG7 type; 55 parts of polyvinyl chloride resin SG8 type; 12 parts of wood powder; 30 parts of heavy calcium; 40 parts of floor recycling materials ; 2.4 parts of calcium stearate; 5 parts of foaming regulator YF-530; 0.4 part of ADC foaming agent; 0.9 part of DC foaming agent; 0.25 part of stearic acid; 0.4 part of oxidized polyethylene wax, internal lubricant HLD- 0.5 part of 60; 0.5 part of external lubricant G31; 3 parts of toughening agent EVA, of which wood flour and heavy calcium need to be activated before use.
[0016] The preparation method of the high-hardness polyethylene floor, the specific steps are as follows:
[0017] Add the polyvinyl chloride resin, wood flour, heavy calcium and floor recycling materials to the hot mixing pot and heat it to 40-55 °C, then add other raw materials to the hot mixing pot, mix evenly an
Example Embodiment
[0018] Example 2
[0019] The high-hardness polyethylene floor is composed of the following materials by weight: 22 parts of polyvinyl chloride resin SG7 type; 54 parts of polyvinyl chloride resin SG8 type; 13 parts of wood powder; heavy calcium 30 parts; 49 parts of floor recycling material; 2.2 parts of calcium stearate; 7 parts of foam regulator YF-530; 0.5 part of ADC foaming agent; 0.9 part of DC foaming agent; 0.2 part of stearic acid; oxidized polyethylene wax 0.5 part, internal lubricant HLD-60 0.4 part; external lubricant G31 0.5 part; toughening agent EVA 2.8 part, among which wood flour and heavy calcium need to be activated before use. The specific steps are the same as those in Example 1. Shore hardness 85HD, bending strength 82MPa.
Example Embodiment
[0020] Example 3
[0021] The high-hardness polyethylene floor is composed of the following materials in parts by weight: 20 parts of polyvinyl chloride resin SG7 type; 50 parts of polyvinyl chloride resin SG8 type; 10 parts of wood powder; 20 parts of heavy calcium; 45 parts of floor recycling materials ; 2.2 parts of calcium stearate; 3 parts of foam regulator YF-530; 0.3 part of ADC foaming agent; 0.8 part of DC foaming agent; 0.2 part of stearic acid; 0.3 part of oxidized polyethylene wax, internal lubricant HLD- 60 0.3 parts; external lubricant G31 0.4 parts; toughening agent EVA 2.4 parts, among which wood flour and heavy calcium need to be activated before use. The specific steps are the same as those in Example 1. Shore hardness 82HD, bending strength 90MPa.
PUM
Property | Measurement | Unit |
---|---|---|
Bending strength | aaaaa | aaaaa |
Bending strength | aaaaa | aaaaa |
Bending strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap