Aluminum button and preparation method thereof
一种纽扣、质感的技术,应用在服装辅料领域,能够解决真实度不够、仿铝质感效果欠佳、金属感差等问题
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0073] The present invention also provides a method for preparing the aluminum texture button described in the above technical solution, comprising the following steps:
[0074] a) mixing unsaturated polyester resin, FX-218 flexible resin liquid, methyl ethyl ketone and cobalt salt, after reaching the gelation time, adding a viscosity modifier to adjust the viscosity to obtain a blank;
[0075] b) making the blank into a blank to obtain a button blank;
[0076] c) Spraying a top coat on the button blank to obtain a button.
[0077] Among them, the unsaturated polyester resin, FX-218 flexible resin liquid, methyl ethyl ketone, cobalt salt, viscosity regulator, and the type and amount of topcoat are all consistent with those described in the above technical solution, and will not be repeated here. The operations in steps a) to c) are consistent with those described in the above technical solution, and will not be repeated here.
[0078] Among them, before the topcoat is spraye...
Embodiment 1
[0082] 1.1 Preparation of billet
[0083] New billet raw material:
[0084] Material A:
[0085] Ortho-phthalic unsaturated polyester resin 988N-1 94%;
[0086] FX-218 flexible resin liquid 6%;
[0087] Material B:
[0088] Methyl ethyl ketone 0.9%;
[0089] Cobalt naphthenate 0.9%;
[0090] Styrene 1.0%.
[0091] New blank preparation:
[0092] Add FX-218 flexible resin liquid to the o-phthalic unsaturated polyester resin, then add the same amount of cobalt salt and methyl ethyl ketone, test the gelation and adjust the gelation time to meet the production requirements, and then add styrene to adjust the viscosity to form a new Blank slurry; made into button blanks according to common button production standards.
[0093] 1.2 Preparation of topcoat
[0094] Main paint formula:
[0095]
[0096] Ingredients:
[0097] The mass ratio of isocyanate curing agent to main paint is 1.0:3.0;
[0098] The mass ratio of diluent to main paint is 2.0:3.0.
[0099] Topcoat p...
Embodiment 2
[0112] 1.1 Preparation of billet
[0113] New billet raw material:
[0114] Material A:
[0115] Ortho-phthalic unsaturated polyester resin 986 96%;
[0116] FX-218 flexible resin liquid 4%;
[0117] Material B:
[0118] Methyl ethyl ketone 0.95%;
[0119] Cobalt naphthenate 0.95%;
[0120] Styrene 1.2%.
[0121] New blank preparation:
[0122] Add FX-218 flexible resin liquid to the o-phthalic unsaturated polyester resin, then add the same amount of cobalt salt and methyl ethyl ketone, test the gelation and adjust the gelation time to meet the production requirements, and then add styrene to adjust the viscosity to form a new Blank slurry; made into button blanks according to common button production standards.
[0123] 1.2 Preparation of topcoat
[0124] Main paint formula:
[0125]
[0126]
[0127] Ingredients:
[0128] The mass ratio of isocyanate curing agent to main paint is 1.2:3.5;
[0129] The mass ratio of diluent to main paint is 2.5:3.5.
[0130] ...
PUM
Property | Measurement | Unit |
---|---|---|
color fastness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap