Preparation method of cobalt oxide coated nickel hydroxide composite material for alkaline rechargeable battery
一种二次电池、氢氧化镍的技术,应用在碱性蓄电池、电池电极、镍蓄电池等方向,达到长使用寿命、提高导电性和循环稳定性、高比容量的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] Example 1 Preparation of Cobalt Oxide Coated Nickel Hydroxide Composite Material for Alkaline Secondary Battery
[0026] (1) Preparation of spherical nickel hydroxide precursor doped with yttrium
[0027] Nickel chloride, cobalt sulfate and yttrium sulfate are according to nickel, cobalt, yttrium molar ratio: nickel 90%, cobalt 7%, yttrium 3% are mixed uniformly the salt solution of the nickel cobalt yttrium of preparation 1 mol / liter, preparation concentration is 3 - Potassium hydroxide solution of 5 mol / liter, and the complexing agent for preparing ammonia concentration of 15% ammonia water, and simultaneously injected into the reaction kettle with stirring and dispersing function for chemical precipitation, wherein the flow rate of the salt solution is 3ml / min , the flow rate of potassium hydroxide is 6ml / min, the flow rate of ammonia solution is 3ml / min, the conditions for controlling the chemical reaction are that the pH is in the range of 11-13, and the temperatur...
Embodiment 2
[0032] Example 2 Preparation of Cobalt Oxide Coated Nickel Hydroxide Composite Material for Alkaline Secondary Battery
[0033] (1) Preparation of spherical nickel hydroxide precursor doped with yttrium
[0034] Nickel chloride, cobalt sulfate and yttrium sulfate are according to nickel, cobalt, yttrium molar ratio: nickel 95%, cobalt 3%, yttrium 2%, mix the salt solution of nickel cobalt yttrium of 2 mol / liter evenly, preparation concentration is 3 - Potassium hydroxide solution of 5 mol / liter, and the complexing agent for preparing ammonia concentration of 25% ammonia water, and simultaneously injected into the reaction kettle with stirring and dispersing function for chemical precipitation, wherein the flow rate of the salt solution is 5ml / min , the flow rate of potassium hydroxide is 8ml / min, the flow rate of ammonia solution is 5ml / min, the conditions for controlling the chemical reaction are that the pH is in the range of 11-13, and the temperature is at 70°C. Wash unti...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap