Novel acrylate modified waterborne polyurethane adhesive
一种水性聚氨酯、丙烯酸酯的技术,应用在聚脲/聚氨酯粘合剂、接枝聚合物粘合剂、胶粘剂等方向,能够解决耐水性差、初黏力小、粘结强度低等问题,达到市场前景广阔、改善粘结性能、缩短固化时间的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
example 1
[0030] 1. Add 26 grams of isophorone diisocyanate (IPDI) and 40 grams of dehydrated polytetrahydrofuran ether glycol (PTMG, 2000) into a 500ml three-neck flask equipped with a stirring blade, a condenser tube and nitrogen protection at 80°C 0.02 g of dibutyltin dilaurate was added as an initiator, and kept at 70-80° C. for 40-50 minutes.
[0031] 2. Add 7 grams of 2,2-dimethylolpropionic acid and react for 2 hours. Acetone can be used to adjust the viscosity during the reaction.
[0032] 3. Lower the temperature so that the temperature in the three-neck flask is 40-48°C, and neutralize by adding triethylamine and a small amount of deionized water.
[0033] 4. After the dispersion is uniform, add 7 grams of sodium lauryl sulfate and 5 grams of potassium persulfate to continue the reaction for 30 minutes.
[0034] 5. After 30 minutes, add 20 grams of butyl acrylate and adjust the temperature to 60° C., and react for 2 hours.
[0035] After 6.2 hours, obtain novel acrylate modi...
example 2
[0037] 1. Add 26.3 grams of toluene diisocyanate (TDI) and 40 grams of dehydrated polytetrahydrofuran ether glycol (PTMG, 2000) into a 500ml three-necked flask equipped with a stirring paddle, condenser and nitrogen protection, and add 0.02 grams of Dibutyltin laurate was used as an initiator, and stirred at 90°C for 40-50 minutes.
[0038] 2. Add 5 grams of 2,2-dimethylolpropionic acid and react for 1 hour. Acetone can be used to adjust the viscosity during the reaction.
[0039] 3. Cool down to 50°C, add 7 grams of sodium lauryl sulfate, 5 grams of azobisisobutyronitrile and 30 grams of hydroxyethyl acrylate, raise the temperature to 80°C, and react for two hours
[0040] 4. Cool down to 40°C, add triethylamine and a small amount of deionized water for neutralization and dispersion, and obtain a new type of acrylate-modified water-based polyurethane binder.
example 3
[0042] 1. Add 43 grams of isophorone diisocyanate (IPDI) and 40 grams of dehydrated polytetrahydrofuran ether glycol (PTMG, 1000) into a 500ml three-neck flask equipped with a stirring blade, a condenser tube and nitrogen protection at 80°C 0.02 g of dibutyltin dilaurate was added as an initiator, and kept at 70-80° C. for 40-50 minutes.
[0043] 2. Add 7 grams of 2,2-dimethylolpropionic acid and react for 2 hours. Acetone can be used to adjust the viscosity during the reaction.
[0044] 3. Lower the temperature so that the temperature in the three-neck flask is 40-48°C.
[0045] 4. Add 10 g of 2-hydroxyethyl methacrylate and continue the reaction for 30 minutes.
[0046] 5. After 30 minutes, add 7 grams of sodium lauryl sulfate, 5 grams of azobisisobutyronitrile and 30 grams of hydroxybutyl acrylate and adjust the temperature to 60°C for 2 hours of reaction.
[0047] 6. After 2 hours, lower the temperature to 40°C and add triethylamine and a small amount of deionized water ...
PUM
Property | Measurement | Unit |
---|---|---|
number average molecular weight | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap