Environment-friendly anti-static floor and manufacturing method thereof
An anti-static floor and environment-friendly technology, applied in the field of floor, can solve the problems of not being able to meet the requirements of floor environmental protection, poor heat insulation effect, poor deformation resistance, etc., to achieve good heat insulation performance, good anti-aging, and ensure stability sexual effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0033] S1. Take 25 parts of pebbles, 2 parts of graphite powder, 28 parts of diatom mud particles, 5 parts of bauxite particles, 25 parts of fly ash, 0.4 parts of polyphenylene particles, 0.8 parts of hollow glass beads, and 0.3 parts of bonding mortar , 0.5 parts of magnesium silicate, 1 part of mineral fiber, and 7 parts of quicklime were placed in a mixer, stirred at a speed of 1000 r / min, and the stirring time was 10 minutes to obtain a mixture;
[0034] S2. Add water to the mixture, the mass ratio of the mixture to water is 2:1, the stirring speed is 200r / min, the stirring time is 10min, and stir evenly to obtain the base material;
[0035] S3. Put the base material in a temperature of 15°C and a humidity of 65%, and let it stand for 15 minutes;
[0036] S4. Add 1 part of impact modifier, 2 parts of antistatic agent and 2 parts of heat stabilizer to the base material in sequence at a speed of 10kg / min, and add impact modifier, antistatic agent and heat stabilizer When th...
Embodiment 2
[0041] S1. Mix 25 parts of pebble powder, 4 parts of graphite powder, 30 parts of diatom mud particles, 5 parts of bauxite particles, 12 parts of fly ash, 0.7 parts of polyphenylene particles, 1 part of hollow glass microspheres, and 0.6 parts of bonding mortar. 1 part, 0.7 part of magnesium silicate, 3 parts of mineral fiber and 9 parts of quicklime are placed in a mixer, stirred at a speed of 1000-2000r / min, and the stirring time is 20min to obtain a mixture;
[0042] S2. Add water to the mixture, the mass ratio of the mixture to water is 2:1, the stirring speed is 300r / min, the stirring time is 25min, stir evenly, and obtain the base material;
[0043] S3. Put the base material in a temperature of 18°C and a humidity of 75%, and let it stand for 30 minutes;
[0044] S4. Add 2 parts of impact modifier, 3 parts of antistatic agent and 4 parts of heat stabilizer to the base material in sequence, the speed of addition is 15kg / min, and add impact modifier, antistatic agent and...
Embodiment 3
[0049] S1. Take 20 parts of pebble powder, 2 parts of graphite powder, 14 parts of diatom mud particles, 12 parts of bauxite particles, 25 parts of fly ash, 2 parts of polyphenylene particles, 4 parts of hollow glass beads, and 1 part of bonding mortar 1 part, 0.8 part of magnesium silicate, 4 parts of mineral fiber and 8 parts of quicklime were placed in a mixer, stirred at a speed of 2000r / min, and the stirring time was 30min to obtain a mixture;
[0050] S2. Add water to the mixture, the mass ratio of the mixture to water is 2:1, the stirring speed is 500r / min, the stirring time is 30min, stir evenly, and obtain the base material;
[0051] S3. Put the base material in a temperature of 20°C and a humidity of 85%, and let it stand for 45 minutes;
[0052] S4. Add 1.2 parts of impact modifier, 3 parts of antistatic agent and 3 parts of heat stabilizer to the base material in sequence at a speed of 20kg / min, and add impact modifier, antistatic agent and heat stabilizer When the ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology