High-strength durable polylactic acid and preparation method thereof
一种聚乳酸、耐久的技术,应用在高强耐久聚乳酸及其制备领域,能够解决聚乳酸力学强度和耐久性差等问题,达到易于操作、工艺简单、力学性能性好的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] High-strength and durable polylactic acid, consisting of 100 parts by weight of polylactic acid (100,000), 5 parts by weight of polyadipate / butylene terephthalate resin, and 3 parts by weight of 2-(3,4-dihydroxyphenyl)ethylamine , 4.5 parts by weight of polycarbonate, 1 part by weight of wood powder, 2 parts by weight of silane coupling agent KH550, 1 part by weight of antioxidant 1010, 1.5 parts by weight of polyethylene wax, 2.5 parts by weight of ethylene-vinyl acetate copolymer, 1 part by weight of wollastonite powder (300 mesh), 0.5 part by weight of ultraviolet absorber UV-9, 1 part by weight of sodium phosphite and 0.5 part by weight of heat stabilizer tris (2,4-di-tert-butylphenyl) phosphite .
[0023] The preparation method of the above-mentioned high-strength and durable polylactic acid is to weigh the raw materials according to the composition and proportion, mix them evenly, and then add them to a twin-screw extruder for blending and extruding to obtain high...
Embodiment 2
[0025] High-strength and durable polylactic acid, consisting of 100 parts by weight of polylactic acid (200,000), 8 parts by weight of polyadipate / butylene terephthalate resin, and 5 parts by weight of 2-(3,4-dihydroxyphenyl)ethylamine , 7.5 parts by weight of polycarbonate, 2 parts by weight of wood flour, 4 parts by weight of silane coupling agent KH550, 3 parts by weight of antioxidant 1010, 3 parts by weight of polyethylene wax, 3 parts by weight of ethylene-vinyl ester copolymer, 2 parts by weight of wollastonite powder (700 mesh), 1.5 parts by weight of ultraviolet absorber UV-9, 3 parts by weight of sodium phosphite and 1 part by weight of heat stabilizer tris (2,4-di-tert-butylphenyl) phosphite .
[0026] The preparation method of the above-mentioned high-strength and durable polylactic acid is to weigh the raw materials according to the composition and proportion, mix them evenly, and then add them to a twin-screw extruder for blending and extruding to obtain high-str...
Embodiment 3
[0028] High-strength and durable polylactic acid, consisting of 100 parts by weight of polylactic acid (250,000), 6 parts by weight of polyadipate / butylene terephthalate resin, and 4 parts by weight of 2-(3,4-dihydroxyphenyl)ethylamine , 6 parts by weight of polycarbonate, 1.5 parts by weight of wood powder, 3 parts by weight of silane coupling agent KH550, 2 parts by weight of antioxidant 1010, 2 parts by weight of polyethylene wax, 2.5 parts by weight of ethylene-vinyl acetate copolymer, 1.5 parts by weight of wollastonite powder (500 mesh), 1 part by weight of ultraviolet absorber UV-9, 2 parts by weight of sodium phosphite and 0.8 parts by weight of heat stabilizer tris (2,4-di-tert-butylphenyl) phosphite .
[0029] The preparation method of the above-mentioned high-strength and durable polylactic acid is to weigh the raw materials according to the composition and proportion, mix them evenly, and then add them to a twin-screw extruder for blending and extruding to obtain h...
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
heat deflection temperature | aaaaa | aaaaa |
melting point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap