[0025] The invention provides a graphene antibacterial film, wherein the main materials used include by weight: 45 parts of graphene oxide, 25 parts of polyurethane resin, 15 parts of polyethersulfone resin, 10 parts of polytetrafluoroethylene resin, 8 parts of polyethylene resin, 50 parts of organic solvent, 5 parts of mugwort extract, 2 parts of sodium carboxymethyl cellulose, 1 part of tea polyphenol and 3 parts of cationic nano-silver antibacterial agent;
[0026] The preparation method of graphene antibacterial film is as follows:
[0027] Step 1: Using graphene oxide as a raw material, using a strong oxidant, under the action of stirring, chemically intercalate graphite, shear peeling, dispersing and refining, and sieve to obtain graphite oxide powder, and prepare cationic nano-silver The antibacterial agent and graphene oxide powder are fully mixed evenly and set aside;
[0028] Step 2: Add the mugwort extract into the organic solvent and stir evenly to obtain an organ...
Embodiment 2
[0038] The invention provides a graphene antibacterial film, wherein the main materials used include by weight: 50 parts of graphene oxide, 28 parts of polyurethane resin, 18 parts of polyethersulfone resin, 13 parts of polytetrafluoroethylene resin, 9 parts of polyethylene resin, 55 parts of organic solvent, 6 parts of mugwort extract, 3 parts of sodium carboxymethyl cellulose, 2 parts of tea polyphenols and 5 parts of cationic nano-silver antibacterial agent;
[0039] The preparation method of graphene antibacterial film is as follows:
[0040] Step 1: Using graphene oxide as a raw material, using a strong oxidant, under the action of stirring, chemically intercalate graphite, shear peeling, dispersing and refining, and sieve to obtain graphite oxide powder, and prepare cationic nano-silver The antibacterial agent and graphene oxide powder are fully mixed evenly and set aside;
[0041]Step 2: Add the mugwort extract into the organic solvent and stir evenly to obtain an orga...
Embodiment 3
[0051] The invention provides a graphene antibacterial film, wherein the main materials used include by weight: 52 parts of graphene oxide, 29 parts of polyurethane resin, 19 parts of polyethersulfone resin, 14 parts of polytetrafluoroethylene resin, 10 parts of polyethylene resin, 53 parts of organic solvent, 7 parts of mugwort extract, 4 parts of sodium carboxymethyl cellulose, 2 parts of tea polyphenols and 5 parts of cationic nano silver antibacterial agent;
[0052] The preparation method of graphene antibacterial film is as follows:
[0053] Step 1: Using graphene oxide as a raw material, using a strong oxidant, under the action of stirring, chemically intercalate graphite, shear peeling, dispersing and refining, and sieve to obtain graphite oxide powder, and prepare cationic nano-silver The antibacterial agent and graphene oxide powder are fully mixed evenly and set aside;
[0054] Step 2: Add the mugwort extract into the organic solvent and stir evenly to obtain an or...
PUM
Property | Measurement | Unit |
---|---|---|
tensile strength | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap