Vinyl acetate-ethylene copolymer emulsion as electrostatic spinning adhesive and synthesis method thereof
一种乙烯共聚乳液、醋酸乙烯的技术,应用在一元羧酸酯共聚物粘合剂、粘合剂类型、对表面涂布液体的装置等方向,能够解决粘接强度不高、耐水性差、手感硬等问题,达到产品性能好、玻璃化温度低、粒子细的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0042] 1. Preparation of raw materials
[0043] 1) Preparation of pre-emulsion: add 80 parts of deionized water to the pre-emulsification tank, start the mixer, add 1.5 parts of composite emulsion (wherein the nonionic emulsifier is octylphenol polyoxyethylene ether (X-100), 0.3 parts , The amphoteric emulsifier is sodium alkylphenol polyoxyethylene ether sulfate (VA-50), 1.2 parts), 0.2 parts of sodium bicarbonate, 0.2 parts of sodium acetate, 5 parts of N-methylolacrylamide, after stirring and dissolving, Add 80 parts of vinyl acetate and 20 parts of butyl acrylate, and stir for 30 minutes to prepare a pre-emulsion;
[0044] 2) Prepare emulsifier solution: add 40 parts of deionized water, 0.1 part of hydroxyethyl cellulose, and 3.3 parts of compound emulsion into the emulsifier tank (the non-ionic emulsifier is octylphenol polyoxyethylene ether (X-100) , 0.5 parts, the amphoteric emulsifier is sodium alkylphenol polyoxyethylene ether sulfate (VA-50), 2.8 parts), start the agi...
Embodiment 2
[0051] Get 120 parts of deionized water, 0.3 part of carboxymethyl cellulose, 6 parts of composite emulsion (wherein the nonionic emulsifier is nonylphenol polyoxyethylene ether (CO-887), 0.8 part, and the amphoteric emulsifier is phenol ether sulfuric acid (NPS930), 5.2 parts), 1.2 parts cumene hydroperoxide, 0.5 parts zinc formaldehyde sulfoxylate, 0.4 parts sodium bicarbonate, 0.2 parts sodium acetate, 7 parts N-methylolacrylamide, 90 parts acetic acid Ethylene, 35 parts of isooctyl acrylate, 20 parts of ethylene, prepare the special VAE of electrostatic flocking with the method of embodiment 1, the result is as follows:
[0052] Exterior
[0053] Glass transition temperature °C
Embodiment 3
[0055] Get 140 parts of deionized water, 0.2 part of hydroxypropyl cellulose, 7 parts of composite emulsion (wherein nonionic emulsifier is octylphenol polyoxyethylene ether (CA-630), 1.0 part, amphoteric emulsifier is alkylphenol Polyoxyethylene ether sulfate sodium salt (VA-50), 6.0 parts), 1.5 parts of tert-butyl hydroperoxide, 0.7 parts of zinc formaldehyde sulfoxylate, 0.3 parts of sodium bicarbonate, 0.4 parts of sodium acetate, 4 parts of N-hydroxy Methacrylamide, 120 parts of vinyl acetate, 40 parts of ethyl acrylate, 30 parts of ethylene, prepare the special VAE for electrostatic flocking with the method of embodiment 1, the result is as follows:
[0056] Exterior
PUM
Property | Measurement | Unit |
---|---|---|
solid containing ratio | aaaaa | aaaaa |
solid containing ratio | aaaaa | aaaaa |
solid containing ratio | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap