Method for preparing lithium-manganese phosphate positive material by adopting wet-chemical method
一种磷酸锰锂、正极材料的技术,应用在电池电极、结构零件、电气元件等方向,能够解决单位设备产率低、副产物分离等问题
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0014] (1) Mix 118.1g of lithium phosphate (Shanghai Zhongli Industrial Co., Ltd., purity 98%) and 412.1g of manganese phosphate crystals (analytically pure, purity 99%) into a mortar, then add 62.5g of absolute ethanol to grind After 3 hours ethanol volatilized completely, the mixture became powder;
[0015] (2) Add 6.25g of pharmaceutical grade ascorbic acid, grind it evenly, then add 625g of 4% polyvinyl alcohol (molecular weight 6000) solution, and stir it evenly on a small disperser to form a slurry;
[0016] (3) Pour the slurry into a hydrothermal reaction kettle, seal it well, heat it to 180°C and keep it for 10 hours, then cool down to room temperature, open the reaction kettle and pour out all the materials, and carry out blast drying at 105°C to form a lump;
[0017] (4) Use a tubular experimental electric furnace to raise the temperature of the block to 450°C at a rate of 5°C / min under the protection of high-purity nitrogen, keep it warm for 2 hours, and then heat i...
Embodiment 2
[0020] (1) Mix 118.1g of lithium phosphate (Shanghai Zhongli Industrial Co., Ltd., purity 98%) and 412.1g of manganous phosphate crystals (analytically pure, purity 99%) into a mortar, then add 62.5g of absolute ethanol to grind After 1.2 hours, the ethanol evaporated completely, and the mixture became powder;
[0021] (2) Add 6.25g of pharmaceutical grade ascorbic acid, grind evenly, then add 625g of 4% polyvinyl alcohol (molecular weight: 15,000) solution, and use a small dispersion disc to stir evenly into a slurry;
[0022] (3) Pour the slurry into a hydrothermal reaction kettle, seal it well, heat it to 180°C and keep it for 10 hours, then cool down to room temperature, open the reaction kettle and pour out all the materials, and carry out blast drying at 105°C to form a block;
[0023] (4) Use a tube-type experimental electric furnace to raise the temperature of the block to 450°C at a rate of 5°C / min under the protection of high-purity nitrogen, keep it for 2 hours, and...
Embodiment 3
[0026] (1) Mix 120.5g of lithium phosphate (Shanghai Zhongli Industrial Co., Ltd., purity 98%) and 412.1g of manganese phosphate crystals (analytically pure, purity 99%) into a mortar, then add 62.5g of absolute ethanol to grind After 3 hours ethanol volatilized completely, the mixture became powder;
[0027] (2) Add 6.25g of pharmaceutical grade ascorbic acid, grind evenly, then add 625g of 4% polyvinyl alcohol (molecular weight 10000) solution, stir evenly to form a slurry;
[0028] (3) Pour the slurry into a hydrothermal reaction kettle, heat to 180°C for 10 hours, then cool down to room temperature, open the reaction kettle, pour out all the materials, and carry out blast drying at 105°C to form lumps;
[0029] (4) Use a tube-type experimental electric furnace to raise the temperature of the block to 450°C at a rate of 5°C / min under the protection of high-purity nitrogen, keep it for 2 hours, and then raise the temperature to 700°C at a rate of 5°C / min for 4 hours. Natura...
PUM
Property | Measurement | Unit |
---|---|---|
molecular weight | aaaaa | aaaaa |
molecular weight | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap