Surface-treated steel plate, fuel pipe, cell can
一种表面处理钢板、电池壳的技术,应用在电池组零部件、电池盒/外套、电池箱/套材料等方向,能够解决不具有耐腐蚀性、针孔点蚀、环境安全性不理想等问题
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0057] As a base, a steel sheet obtained by annealing a cold-rolled sheet (0.25 mm in thickness) of low-carbon aluminum-killed steel having the chemical composition shown below was prepared.
[0058] C: 0.045% by weight, Mn: 0.23% by weight, Si: 0.02% by weight, P: 0.012% by weight, S: 0.009% by weight, Al: 0.063% by weight, N: 0.0036% by weight, remainder: Fe and unavoidable Impurities
[0059] Then, the prepared steel sheet was subjected to alkaline electrolytic degreasing and acid pickling by immersion in sulfuric acid, and then nickel plating was performed under the following conditions to form a nickel plating layer with a thickness of 0.5 μm.
[0060] Bath composition: nickel sulfate 250g / L, nickel chloride 45g / L, boric acid 30g / L
[0061] pH: 3~4.8
[0062] Bath temperature: 60°C
[0063] Current density: 10A / dm 2
[0064] Next, heat-treat the steel plate with the nickel coating for two hours at a temperature of 650°C and a non-oxidizing atmosphere (vacuum annealin...
Embodiment 2
[0066] A surface-treated steel sheet was produced in the same manner as in Example 1 except that the heat treatment time was changed to 4 hours and evaluated in the same manner. The results are shown in Table 1.
Embodiment 3
[0068] A surface-treated steel sheet was produced in the same manner as in Example 2 except that the thickness of the nickel plating layer was 1 μm, and was evaluated in the same manner. The results are shown in Table 1.
PUM
Property | Measurement | Unit |
---|---|---|
current density | aaaaa | aaaaa |
current density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap