Ceramics particle strengthened composite material lining metal tube and manufacturing method thereof
一种陶瓷颗粒、复合材料的技术,应用在复合耐磨管领域,能够解决热固性塑料耐腐蚀性能差、塑料和钢管间结合力低、易发生变形和脱落等问题,达到耐磨性和耐蚀性提升、制造工艺简单、便于批量生产的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0040] Refer to attached figure 1 , weigh 50 kg of 180-mesh industrial alumina particles, immerse in an aqueous solution containing KH-550 silane coupling agent with a mass fraction of 5%, stir for 1 hour, filter and dry; 1000 parts of 4,4'-diphenyl A mixture of methane diisocyanate (MDI) and 500 parts of polyester diol as a polyurethane prepolymer, mixed with the above-mentioned pretreated alumina particles, stirred for 2 hours and then added 80 parts of 1,4-butanediol (BD) , after uniform stirring, the polyurethane liquid castable is obtained.
[0041] refer to figure 2 , image 3 and Figure 4 , the manufacture of composite material-lined metal pipes: first evenly paint a layer of rubber-metal adhesive on the inner wall of the stainless steel seamless steel pipe, that is, the outer casing 1, and then place it on four rollers 5 in a large oven, among which A drum rotates at 300 rpm. When the jacket steel pipe is heated to 90°C, keep the constant temperature, extend int...
Embodiment 2
[0044] Refer to attachedfigure 1 , weighing 100 kg of 300-mesh industrial quartz sand particles, immersed in an aqueous solution containing 5% KH-550 silane coupling agent, stirred for 1 hour, filtered and dried; 1000 parts of M5050 type Polyurethane prepolymer (the main component is 4,4'-diphenylmethane diisocyanate), mixed with the above-mentioned pretreated quartz sand particles, stirred for 1.5 hours and then added 50 parts of 1,4-butanediol (BD), After uniform stirring, the polyurethane liquid castable is prepared.
[0045] Coat the inner wall of stainless steel seamless steel pipe evenly with 218 type rubber metal adhesive from Chemlok, and then place it on four rollers in a large oven, one of which rotates at 500 rpm turn. When the jacket steel pipe is heated to 100°C, keep the temperature constant, extend into the pouring pipe with slots below, inject the liquid castable into the pouring pipe under a certain pressure, make the liquid castable squeeze out along the slo...
PUM
Property | Measurement | Unit |
---|---|---|
Shore hardness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap