UV frosted ink
一种磨砂油墨、磨砂粉的技术,应用在印刷油墨领域,能够解决凹印印刷方式限制等问题,达到降低生产制备成本、操作方便快捷、降低生产成本的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0021] Embodiment one, a kind of UV matte ink, comprises following raw material composition: curing resin, UV varnish, active agent, photoinitiator and additive;
[0022] The weight ratio of each raw material component is: 30 parts of cured resin, 10 parts of UV varnish, 40 parts of active agent, 2 parts of photoinitiator, and 10 parts of additive;
[0023] The activating agent is formed by mixing a reactive diluent and a surfactant, and the weight percentages of the reactive diluent and the surfactant are 87% and 13% respectively;
[0024] The additive is formed by mixing dispersant, polymerization inhibitor and leveling agent with grinding powder, and the mixing mass percentage of grinding powder and dispersant, polymerization inhibitor and leveling agent is 79%: 7%: 7%: 7% ;
[0025] The scrub powder is mixed with wax powder and calcium carbonate 1:1;
[0026] The preparation method of described a kind of UV matte printing ink, comprises the steps:
[0027] Step 1: Weigh...
Embodiment 2
[0030] Embodiment two, a kind of UV matte ink, comprises following raw material composition: curing resin, UV varnish, active agent, photoinitiator and additive;
[0031] The weight ratio of each raw material component is: 40 parts of cured resin, 15 parts of UV varnish, 55 parts of active agent, 5 parts of photoinitiator, and 15 parts of additive;
[0032] The activating agent is formed by mixing a reactive diluent and a surfactant, and the weight percentages of the reactive diluent and the surfactant are 87% and 13% respectively;
[0033] The additive is formed by mixing dispersant, polymerization inhibitor and leveling agent with grinding powder, and the mixing mass percentage of grinding powder and dispersant, polymerization inhibitor and leveling agent is 79%: 7%: 7%: 7% ;
[0034] The scrub powder is mixed with wax powder and calcium carbonate 1:1;
[0035] The preparation method of described a kind of UV matte printing ink, comprises the steps:
[0036] Step 1: Weigh...
Embodiment 3
[0039] Embodiment three, a kind of UV matte ink, comprises following raw material composition: curing resin, UV varnish, active agent, photoinitiator and additive;
[0040] The weight ratio of each raw material component is: 35 parts of cured resin, 13 parts of UV varnish, 48 parts of active agent, 3 parts of photoinitiator, and 12 parts of additive;
[0041] The activating agent is formed by mixing a reactive diluent and a surfactant, and the weight percentages of the reactive diluent and the surfactant are 87% and 13% respectively;
[0042] The additive is formed by mixing dispersant, polymerization inhibitor and leveling agent with grinding powder, and the mixing mass percentage of grinding powder and dispersant, polymerization inhibitor and leveling agent is 79%: 7%: 7%: 7% ;
[0043] The scrub powder is mixed with wax powder and calcium carbonate 1:1;
[0044] The preparation method of described a kind of UV matte printing ink, comprises the steps:
[0045] Step 1: Wei...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap