PVC low-foamed board and manufacturing method thereof
一种低发泡、板材的技术,应用在建筑装饰材料领域,能够解决PVC发泡板材制作工艺复杂、成本高、力学性能不稳定等问题,达到良好经济效益、增强机械强度、降低生产成本的效果
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0027] According to the weight ratio, select 100 parts of S-700 PVC resin, 80 parts of active light calcium, 5 parts of composite lead salt stabilizer, 1.2 parts of stearic acid, 0.6 parts of oxidized polyethylene wax, and external lubricant. 0.46 parts of polyethylene wax, 0.64 parts of foaming agent AC, NaHCO 3 2.2 parts, 8 parts of ACM-01 impact modifier, 21 parts of acrylic foaming regulator, 120 parts of regrind. Add all the above-mentioned materials into a high-speed mixer, heat to 90-120°C, keep the temperature for 15 minutes, and stir evenly at high speed. After cold mixing to 25-45℃, the materials are discharged into the silo and extruded by the twin-screw extruder. The materials are foamed through the improved mold and formed together with the grid cloth laid flat in the center of the mold to form the upper and lower layers It is a PVC foam layer, and the core layer is a three-layer reinforced structure of grid cloth. After vacuum setting, cooling forming, traction an...
Embodiment 2
[0031] According to the weight ratio, select 100 parts of S-700 PVC resin, 60 parts of active light calcium, 5 parts of calcium zinc stabilizer, 1.0 part of calcium stearate, 0.5 part of oxidized polyethylene wax as internal lubricant, and 0.5 part of external lubricant. 0.55 parts of polyethylene wax, 0.60 parts of foaming agent AC, NaHCO 3 It is 2.3 parts, 9 parts of ACM-01 impact modifier, 20 parts of acrylic foaming modifier, 100 parts of regrind. Add all the above-mentioned materials into a high-speed mixer, heat to 90-120°C, keep the temperature for 15 minutes, and stir evenly at high speed. After cold mixing to 25-45℃, the materials are discharged into the silo and extruded by the twin-screw extruder. The materials are foamed through the improved mold and formed together with the grid cloth laid flat in the center of the mold to form the upper and lower layers It is a PVC foam layer, and the core layer is a three-layer reinforced structure of grid cloth. After vacuum set...
Embodiment 3
[0035] According to the weight ratio, select 100 parts of S-700 PVC resin, 10 parts of active light calcium, 4 parts of organic tin stabilizer, 0.5 parts of stearic acid for internal lubricant, 0.6 parts of oxidized polyethylene wax, and paraffin wax for external lubricant 0.8 part, 0.4 part of polyethylene wax, 0.5 part of AC as blowing agent, NaHCO 3 2.4 parts, 12 parts of ACM-01 impact modifier, 18 parts of acrylic foaming modifier, 80 parts of regrind. Add all the above-mentioned materials into a high-speed mixer, heat to 90-120°C, keep the temperature for 15 minutes, and stir evenly at high speed. After cold mixing to 25-45℃, the materials are discharged into the silo and extruded by the twin-screw extruder. The materials are foamed through the improved mold and formed together with the grid cloth laid flat in the center of the mold to form the upper and lower layers It is a PVC foam layer, and the core layer is a three-layer reinforced structure of grid cloth. After vacuu...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap